Premium Cast Digital Film with FLITE Technology®

With an easy release liner maintaining the integrity of your graphics, SLX Cast Wrap will allow you to get more wraps out the door with less manpower. The superior repositionability of SLX Cast Wrap + FLITE Technology® provides a long-term bond where it counts: deep channels, complex curves, and rivets. Outperforming other films, your customers will love their visually striking wraps and you’ll love the easy and clean removability.

Arlon SLX Wrap Media

Ideal for full or partial vehicle and fleet wraps, and large decals.
Fast, easy application for the novice and experienced installers.
Vibrant and reliable print quality on Eco-Solvent, Solvent, UV and Latex print systems.
Easy liner release maintaining the integrity of the graphic.

Property	Test Methods	Typical Value
Surface Finish	Gloss Meter 60° Reflection	70 to 90 Gloss Units
Thickness	Micrometer, Federal Bench Type	2-mil (50 micron)
Tensile Strength	Tensile Tester with 2-in (51 mm) jaw separation; crosshead speed of 12 in/min. (5.1 mm/s), web direction	≥ 4.5 lb/in	≥ 0.8 kg/cm
Elongation	Instron Tensile Tester as above	Average 190%
Shelf Life (In Box)	Ideal Storage Temperature 70°F (21°C) and 50% relative humidity	2 years from factory shipment
Application Temperature Range	On clean, dry substrate	40°F to 100°F	4.4°C to 38°C
Application Temperature Range	On clean, dry substrate (corrugated with rivets and channels)	60°F to 100°F	15°C to 38°C
Service Temperature Range	On clean, dry substrate	-40°F to 176°F	-40°C to 80°C
Dimensional Stability	158°F (70°C), 48 hours	0.010 in	0.24 mm
Peel Adhesion	PSTC-1, 15 min, 70°F (21°C)	≥ 2.4 lb/in	≥ 420 N/m
Peel Adhesion	PSTC-1, 24 hours, 70°F (21°C)	≥ 3.0 lb/in	≥ 525 N/m
Peel Adhesion	PSTC-1, 1 week, 70°F (21°C)	≥ 4.2 lb/in	≥ 736 N/m
Liner Release	TLMI Release at 90˚, 300 in/min (760 cm/min)	50 g/2 in	9.84 g/cm
Liner Weight	On a clean, dry substrate	0	0